Voco Polofil Supra Syringe Refills

• Transverse strength: 140 MPa
• Compressive strength: 360 MPa
• Translucency: natural
• Radiopacity: 200 %Al
• Water absorption: 22.9 μg / mm3
• Water solubility: 0.1 μg / mm3
• Polymerization shrinkage: 2.6 % vol.
• Colour stability: no discolouration

Preparation:

• Begin by preparing the tooth according to standard dental procedures. Clean and disinfect the tooth surface thoroughly.

Isolation:

• Isolate the treatment area using a rubber dam or other appropriate isolation method to prevent contamination.

Etching (If Necessary):

• If using an etch-and-rinse adhesive system, apply a suitable etchant on the enamel and dentin surfaces, following the manufacturer's instructions. Rinse and dry thoroughly.

Solobond M Application (If Used):

• Apply Solobond M total-etch bond as per the manufacturer's instructions, ensuring even coverage on the prepared tooth surface. Allow it to sit for the recommended time.

Polofil Supra Application:

• Dispense the desired shade of Polofil Supra from the syringe refill directly onto the prepared tooth surface.
• Use suitable instruments to shape and sculpt the material to achieve the desired anatomical form.
• Ensure even distribution and adaptation of the composite.

Light Curing:

• Use a dental curing light with appropriate wavelength and intensity to cure the Polofil Supra composite. Follow the recommended curing time provided by the manufacturer.

Finishing and Polishing:

• Once the composite is fully cured, use dental finishing and polishing instruments to refine the restoration's surface. Achieve the desired contour and texture.

Final Inspection:

• Inspect the restoration for any irregularities, ensuring it meets aesthetic and functional requiremen

• High Filler Content: 76.5% by weight for robust and durable restorations.
• Micro and Macro Fillers: Combination for limited shrinkage and high resistance to abrasion.
• Superior Aesthetics: Available in seven shades, providing natural-looking results.
• Efficient Handling: Non-sticky consistency, high resistance to light, and good packability for streamlined procedures.
• Radiopacity: 200 %Al for easy differentiation between restoration and natural tooth structure.
• Excellent Physical Properties: Including high transverse and compressive strength for long-term stability.
• Versatile Application: Suitable for aesthetic anterior and posterior restorations, as well as core build-ups.
• High Filler Content: 76.5% by weight for robust and durable restorations.
• Micro and Macro Fillers: Combination for limited shrinkage and high resistance to abrasion.
• Superior Aesthetics: Available in seven shades, providing natural-looking results.
• Efficient Handling: Non-sticky consistency, high resistance to light, and good packability for streamlined procedures.
• Radiopacity: 200 %Al for easy differentiation between restoration and natural tooth structure.
• Excellent Physical Properties: Including high transverse and compressive strength for long-term stability.
• Versatile Application: Suitable for aesthetic anterior and posterior restorations, as well as core build-ups.High Filler Content: 76.5% by weight for robust and durable restorations.
• Micro and Macro Fillers: Combination for limited shrinkage and high resistance to abrasion.
• Superior Aesthetics: Available in seven shades, providing natural-looking results.
• Efficient Handling: Non-sticky consistency, high resistance to light, and good packability for streamlined procedures.
• Radiopacity: 200 %Al for easy differentiation between restoration and natural tooth structure.
• Excellent Physical Properties: Including high transverse and compressive strength for long-term stability.
• Versatile Application: Suitable for aesthetic anterior and posterior restorations, as well as core build-ups.