Voco Polofil Nht Flow Syringe Refills

• Composite Type: Nano-Hybrid Flowable
• Filler Content: > 76% w/w
• Polymerization Shrinkage: < 3.2%
• Surface Hardness (MHV): > 115
• Resistance to Abrasion (ACTA): < 35 µm
• Recommended Indications: - Minimally Invasive Cavities (All Classes) - Class I Cavities - Extended Fissure Sealing - Class II-V Cavities - Undercut Blocking - Lining/Coating Cavities - Repairing Fillings/Veneers - Luting Translucent Prosthetic Pieces
• Application: Thixotropic - "Flows on demand"
• Adhesion Strength (Enamel): 28.1 MPa*
• Adhesion Strength (Dentine): 32.0 MPa*
• Shades: A1, A2, A3

Preparation:

• Ensure the tooth surface is clean, dry, and free from debris.
• Select the appropriate shade of Polofil NHT Flow.

Etching (if required):

• Apply a dental etchant to the enamel and/or dentin surfaces as per standard protocol.
• Rinse thoroughly and dry with an air syringe.

Bonding:

• Apply an adhesive bonding agent (e.g., Bondfix or Solobond M) following the manufacturer's instructions.

Application of Polofil NHT Flow:

• Load the composite into a dispensing instrument.
• Apply the material into the prepared cavity or onto the surface to be restored.

Modeling:

• Use appropriate instruments to shape and contour the composite to achieve the desired anatomical form.

Light Curing:

• Cure the material using a suitable dental curing light according to the manufacturer's recommended time and intensity.

Finishing and Polishing:

• After curing, finish the restoration using appropriate finishing instruments.
• Polish the surface to achieve the desired smoothness and aesthetics.

Check Occlusion:

• Verify the occlusion to ensure proper alignment and function.

Final Inspection:

• Examine the restoration for any irregularities or imperfections.

Post-Operative Instructions:

• Provide the patient with post-operative care instructions for their newly restored tooth.

• Ideal flowability
• Outstanding physical properties
• Excellent wetting properties
• Very high filler content (> 76 % w/w)
• Significantly less polymerisation shrinkage (3.2 %)
• Extremely high resistance to abrasion (ACTA < 35 μm)
• Ideal flowability
• Outstanding physical properties
• Excellent wetting properties
• Very high filler content (> 76 % w/w)
• Significantly less polymerisation shrinkage (3.2 %)
• Extremely high resistance to abrasion (ACTA < 35 μm)