Vincismile TopCEM Dual Cure Resin Cement

Flexural Strength (MPa):

• Dual Cure: >50 MPa
• Self Cure: >50 MPa
• TopCEM Dual Cure: 112.7 MPa
• TopCEM Self Cure: 107.5 MPa

Solubility (μg/mm³):

• Dual Cure: <7.5 μg/mm³
• TopCEM Dual Cure: 1.8 μg/mm³

Water Absorption (μg/mm³):

• Dual Cure: <40 μg/mm³
• TopCEM Dual Cure: 19.8 μg/mm³

Film Thickness (μm):

• <50 μm
• TopCEM: 20 μm

Work Time (23±1°C):

• 60 seconds
• TopCEM: Qualified

Setting Time (37±1°C):

• <10 minutes
• TopCEM: 2 minutes and 38 seconds

Radiopaque Resistance (%):

• 100%

Preparation:

• Ensure that the restoration and tooth surface are clean and free from debris.
• Evaluate the fit of the restoration before cementation.

Mixing:

• Dispense the required amount of TopCEM Dual Cure resin cement onto a mixing pad.
• Mix thoroughly according to the manufacturer's instructions to achieve a homogenous consistency.

Application:

• Apply a thin layer of the mixed cement onto the internal surface of the restoration.
• Seat the restoration onto the prepared tooth surface, ensuring proper alignment and fit.
• Remove excess cement with a suitable instrument.

Curing:

• For dual-cure option: Light cure the cement for the recommended time using a suitable dental curing light.
• For light-cure option: Allow the cement to self-cure or light cure as per preference and clinical requirements.

Finishing:

• Check and adjust occlusion as needed.
• Polish the restoration and surrounding tooth surfaces to achieve a smooth finish.

Post-Operative Care:

• Instruct the patient on proper oral hygiene practices.
• Schedule follow-up appointments for evaluation and maintenance.

• Dual-cure versatility for various applications.
• Fast and efficient working and setting times.
• High flexural strength for durable restorations.
• Low solubility and water absorption rates.
• Wide range of shades for esthetic matching.
• Exceptional radiopacity for accurate diagnosis.
• Strong bonding to multiple dental substrates.
• Dual-cure versatility for various applications.
• Fast and efficient working and setting times.
• High flexural strength for durable restorations.
• Low solubility and water absorption rates.
• Wide range of shades for esthetic matching.
• Exceptional radiopacity for accurate diagnosis.
• Strong bonding to multiple dental substrates.