Prevest Fusion Core Dc Flo (9gm)

Technical Data:

1) Working Time : 60 sec.
2) Setting Time : 3 - 4 min.
3) Compressive Strength : 140 - 150 MPa.
4) Flexural Strength : 60 - 70 MPa.
5) Film Thickness : 50 µm

Composition :

Base Paste : Bisphenol A Glycidyle Methacrylate, Ethoxylated Bisphenol A Dimethacrylate, Triethylene Glycol Dimethacrylate, Silanated Barium Glass Powder, Amorphous Fumed Silica, Curing Agents and Stabilizers.

Catalyst Paste : Bisphenol A Glycidyle Methacrylate, Ethoxyated Bisphenol A Dimethacrylate, Ethoxlated, Triethylene Glycol Dimethacrylate, Silanated Barium Glass Powder, Amorphous Fumed Silica, Curing Agents and Stabilizers

Cautions : Use of zinc oxide, eugenol containing materials must be avoided.

Storage Conditions : Store at temperature between 10°C to 24°C. Close the cap carefully after use. Keep away from moisture. Shelf life not affected after opening if stored in a cool dry place.

Shelf Life : 2 years from the date of manufacturing.

• Sufficiently dry the working area.
• Prepare the cavity suitably for the restorative treatment and should be minimally invasive in order to protect healthy dental hard tissue.
• Clean and dry the cavity.
• Protect the pulp suitably with a light cure cavity liner preferably with Cal LC or Fusion I-Seal.
• Apply Fusion Bond DC to the prepared cavity.
• Remove the cartridge cap and attach a mixing tip.
• Attach intra oral tip if required.
• Place matrix around the prepared tooth and apply Fusion Core DC Flo directly from the cartridge.
• Allow 3-4 minutes for the material to set properly.
• Light cure for 40 sec.
• Restoration can be finished immediately after light curing.

• Light curing for time saving application
• Additional chemical curing for complete polymerisation
• Low heat development even in bulk application
• Flowable, non slumping formula for convenient placement
• Low shrinkage properties
• Light curing for time saving application
• Additional chemical curing for complete polymerisation
• Low heat development even in bulk application
• Flowable, non slumping formula for convenient placement
• Low shrinkage properties