AVUE AvueCore Nano - Dual Cure Flowable Core Buildup composite with Nano Zirconium Dioxide

Dual cure flowable composite with nano zirconium dioxide & calcium fluoride

 If the remaining tooth structure is inadequate for permanent retention of a direct core build-up material, a root post must be used for retaining the core. Retention & support must be derived from within the root canal  because little coronal dentin remains

Ensures a monoblock restoration

This material can be used as 3 in 1 for post, core & crown cementation, leading to less interfaces between the restoration which ultimately unify the tooth directing all the occlusal forces perpendicular to the tooth surface

Benefits of Nano-zirconium dioxide, nano-calcium Flouride Particles

AvueCore Nano is a dual cure high radiopaque  flowable composite material with nano particles  for core-build-up and cementation of posts.it Improves the composite’s physical properties and flow characteristics making AvueCore Nano more strong and durable.

Zirconia particles acts as binder which results in fewer microcracks and increases the fracture toughness 

Ferrule-Only the rule to follow in core build up

Crown preparations exhibiting parallel walls with proper taper and height, coupled with adequate ferrule 1 mm to 2 mm beyond the core material itself without violation of biological width, have historically proven to be clinically successful regardless of the material chosen for the definitive crown

Excellent mechanical properties

Due to its excellent mechanical properties final crown preparation can be carried out more precisely. AvueCore Nano is also suitable for cementing of crowns and bridges, inlays and onlays if there are no high esthetic requirements.

Delivered in 1:1 Smartmix – syringes AvueCore Nano can be easily dispensed and applied directly into the root cana;. AvueCore Nano exhibits a short setting time without high heat generation. The dual cure properties enables the dentist, also to carry out cementations and core build-ups in cases where a light cure cannot be guaranteed to be sufficient.Compressive strength of AvueCore Nano is 320MPa-Flexural strength-145MPa and Diametral Tensile strength-40MPa

Low film thickness

Film thickness of Avuecore Nano is less then 25 microns which ensures proper luting of the post and of crowns &bridges

Dentin like cutability 

This features helps while preparing the tooth , the clinician will get smooth notch-free surface and finishing margins due to its hardness is equal to dentin Compressive strength-320MPa

Benefits

• Excellent compressive strength via incorporating Nano zirconia Dioxide & Nano calcium Fluoride.
• Reinforces the tooth structures when there is insufficient tooth to withstand occlusion laod. 
• Dual cure options to be used in Post cementation insures complete polymerization in areas where curing lights is unable to reach.
• Optimum flowability – Easy to use with Intraoral tips & Endo tips for completely 
• Dentin like cutability.
• Adequate film thickness and flexural strength.
• Reinforces the tooth
• Ease of excess removal
• Superior Handling properties
• Compressive strength-320MPa
• Flexural strength-145MPa
• Diametral Tensile strength-40MPa
• Film thickness-</=25µ